Fortune Steel & Alloys is Specialist approved manufacturer, supplier & exporter of Socket Weld Fittings known for competitive pricing & require minimum time to deliver Socket Weld Fittings at you doorstep. Our Socket Weld Fittings come in a variety of classes and material grades for any application. Socket Weld fittings are available in class 3000, 6000 and 9000 and are manufactured in compliance with ASME 16.11, MSS SP-79, 83, 95, 97, BS 3799
We are socket weld fittings manufacturers in india which are available in all major stainless steel, carbon steel and alloy steel grades. We offer various types of forged Socket Weld 90 Deg Elbow, Socket Weld 45 Deg Elbow, Socket Weld Equal Tee, Socket Weld Unequal Tee, Socket Weld Cross, Socket Weld Unequal Cross, Socket Weld Half Coupling, Socket Weld Full Coupling, Socket Weld Cap. We also manufacture and supply fittings specially manufactured to meet your custom requirements in a variety of stainless steel and special alloy grades.
Standard : ASTM A182/ ASME SA182
Grades : 304, 304L, 304H, 309S, 309H, 310S, 310H, 316, 316TI, 316H, 316L, 316LN, 317, 317L, 321, 321H, 347, 347H, 904L
Dimensions : ANSI B16.11, MSS SP-79, 83, 95, 97, BS 3799
Type : Socket Weld (S/W) & SCREWED (SCRD) – NPT, BSP, BSPT / Threaded
Size : 1/2″ NB TO 4″ NB
Pressure : 2000LBS, 3000LBS, 6000LBS, 9000LBS, etc
Chemical Composition | |||||||||||
Grade | Applicable Standards | C max | Si max | Mn max | P max | S max | Ni | Cr | Mo | Others | |
304 | GB 0Cr18Ni9 | 0.07 | 1.00 | 2.00 | 0.035 | 0.030 | 8.00 - 11.00 | 17.00 - 19.00 | - | - | |
JIS SUS304 | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 8.00 - 11.00 | 18.00 - 20.00 | - | - | ||
BS 304S18 | 0.06 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 9.0 - 12.0 | 17.0 - 19.0 | - | - | ||
ASTM TP304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 8.0 - 11.0 | 18.0 - 20.0 | - | - | ||
DIN 1.4301 | 0.07 | 1.0 | 2.0 | 0.045 | 0.030 | 8.5 - 10.5 | 17.0 - 19.0 | - | - | ||
304L | GB 00Cr19Ni10 | 0.03 | 1.00 | 2.00 | 0.035 | 0.030 | 8.00 - 12.00 | 18.00 - 20.00 | - | - | |
JIS SUS304L | 0.030 | 1.00 | 2.00 | 0.040 | 0.030 | 9.00 - 13.00 | 18.00 - 20.00 | - | - | ||
BS 304S14 | 0.03 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 10.0 - 13.0 | 17.0 - 19.0 | - | - | ||
ASTM TP304L | 0.035 | 1.00 | 2.00 | 0.045 | 0.030 | 8.0 - 13.0 | 18.0 - 20.0 | - | - | ||
DIN 1.4306 | 0.03 | 1.0 | 2.0 | 0.045 | 0.030 | 10.0 - 12.5 | 18.0 - 20.0 | - | - | ||
321 | GB 0Cr18Ni9Ti | 0.12 | 1.00 | 2.00 | 0.035 | 0.030 | 8.00 - 11.00 | 17.00 - 19.00 | - | Ti: 5(C - 0.02) - 0.08 | |
JIS SUS321 | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 9.00 - 13.00 | 17.00 - 19.00 | - | Ti > 5xC | ||
BS 321S18 | 0.08 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 10.0 - 13.0 | 17.0 - 19.0 | - | Ti: 5xC - 0.06 | ||
ASTM TP321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 9.0 - 12.0 | 17.0 - 19.0 | - | Ti: 5(C + N) - 0.07 | ||
DIN 1.4541 | 0.08 | 1.0 | 2.0 | 0.045 | 0.030 | 9.0 - 12.0 | 17.0 - 19.0 | - | Ti: 5xC - 0.07 | ||
316 | GB 0Cr17Ni12Mo2 | 0.08 | 1.00 | 2.00 | 0.035 | 0.030 | 11.00 - 14.00 | 16.00 - 18.50 | 2.00 - 3.00 | - | |
JIS SUS316 | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 10.00 - 14.00 | 16.00 - 18.00 | 2.00 - 3.00 | - | ||
BS 316S18 | 0.07 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 11.0 - 14.0 | 16.0 - 18.5 | 2.0 - 3.0 | - | ||
ASTM TP316 | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 11.00 - 14.00 | 16.0 - 18.0 | 2.00 - 3.00 | - | ||
DIN 1.4401 | 0.07 | 1.0 | 2.0 | 0.045 | 0.030 | 10.5 - 13.5 | 16.5 - 18.5 | 2.0 - 2.5 | - | ||
316L | GB 00Cr17Ni14Mo2 | 0.03 | 1.00 | 2.00 | 0.035 | 0.030 | 12.00 - 15.00 | 16.00 - 18.00 | 2.00 - 3.00 | - | |
JIS SUS316L | 0.030 | 1.00 | 2.00 | 0.040 | 0.030 | 12.00 - 16.00 | 16.00 - 18.00 | 2.00 - 3.00 | - | ||
BS 316S14 | 0.03 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 12.0 - 15.0 | 16.0 - 18.5 | 2.0 - 3.0 | - | ||
ASTM TP316L | 0.035 | 1.00 | 2.00 | 0.045 | 0.030 | 10.00 - 14.00 | 16.0 - 18.0 | 2.00 - 3.00 | - | ||
DIN 1.4404 | 0.030 | 1.0 | 2.0 | 0.045 | 0.030 | 11.0 - 14.0 | 16.5 - 18.5 | 2.0 - 2.5 | - | ||
347 | GB 0Cr18Ni11Nb | 0.08 | 1.00 | 2.00 | 0.035 | 0.030 | 9.00 - 13.00 | 17.00 - 19.00 | - | Nb+Ta: 10xC - 1.00 | |
JIS SUS347 | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 9.00 - 13.00 | 17.00 - 19.00 | - | Nb >10xC | ||
BS 347S18 | 0.08 | 0.20 - 1.00 | 0.50 - 2.00 | 0.040 | 0.030 | 10.0 - 13.0 | 17.0 - 19.0 | - | Nb: 10xC~20XC - 1.00 | ||
ASTM TP347 | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 9.0 - 13.0 | 17.0 - 19.0 | - | Nb: 10xC - 1.10 | ||
DIN 1.4550 | 0.08 | 1.0 | 2.0 | 0.045 | 0.030 | 9.0 - 12.0 | 17.0 - 19.0 | - | Nb: 10xC - 1.00 | ||
310S | GB 0Cr25Ni20 | 0.08 | 1.00 | 2.00 | 0.035 | 0.030 | 19.00 - 22.00 | 24.00 - 26.00 | - | - | |
JIS SUS310S | 0.08 | 1.50 | 2.00 | 0.040 | 0.030 | 19.00 - 22.00 | 24.00 - 26.00 | - | - | ||
BS - | - | - | - | - | - | - | - | - | - | ||
ASTM TP310S | 0.08 | 1.00 | 2.00 | 0.045 | 0.030 | 19.0 - 22.0 | 24.0 - 26.0 | - | - | ||
DIN - | - | - | - | - | - | - | - | - | - | ||
316Ti | GB 0Cr18Ni12Mo2Ti | 0.08 | 1.00 | 2.00 | 0.035 | 0.030 | 11.00 - 14.00 | 16.00 - 19.00 | 1.80 - 2.50 | Ti: 5xC - 0.07 | |
JIS SUS316Ti | 0.08 | 1.00 | 2.00 | 0.040 | 0.030 | 10.00 - 14.00 | 16.00 - 18.00 | 2.00 - 3.00 | Ti > 5xC | ||
BS - | - | - | - | - | - | - | - | - | - | ||
ASTM TP316Ti | 0.08 | 0.75 | 2.00 | 0.045 | 0.030 | 10.0 - 14.0 | 16.0 - 18.0 | 2.00 - 3.00 | Ti: 5(C + N) - 0.07 | ||
DIN 1.4571 | 0.08 | 1.0 | 2.0 | 0.045 | 0.030 | 10.5 - 13.5 | 16.5 - 18.5 | 2.0 - 2.5 | Ti: 5xC - 0.07 |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.0 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
Standard : ASTM A182/ ASME SA182
Grades : UNS S32205, UNS S31803, UNS S32750, UNS S32760
Dimensions : ANSI B16.11, MSS SP-79, 83, 95, 97, BS 3799
Type : Socket Weld (S/W) & SCREWED (SCRD) – NPT, BSP, BSPT / Threaded
Size : 1/2″ NB TO 4″ NB
Pressure : 2000LBS, 3000LBS, 6000LBS, 9000LBS, etc
Manufactured Socket Weld Fittings go with quality assurance test under professionals some of the tests are:
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Fe |
S31803 | 0.030 max | 2.00 max | 1.00 max | 0.030 max | 0.020 max | 22.0 – 23.0 | 3.0 – 3.5 | 4.50 – 6.50 | 0.14 – 0.20 | 63.72 min |
S32205 | 0.030 max | 2.00 max | 1.00 max | 0.030 max | 0.020 max | 21.0 – 23.0 | 2.50 - 3.50 | 4.50 – 6.50 | 0.8 – 0.20 | 63.54 min |
S32750 | 0.030 max | 1.20 max | 0.80 max | 0.035 max | 0.020 max | 24.00 – 26.00 | 3.00 – 5.00 | 6.00 – 8.00 | 0.24 – 0.32 | 58.095 min |
S32760 | 0.05 max | 1.00 max | 1.00 max | 0.030 max | 0.010 max | 24.00 – 26.00 | 3.00 – 4.00 | 6.00 – 8.00 | 0.20 – 0.30 | 57.61 min |
Grade | Density (g/cm 3) | Density (lb/in 3) | Melting Point (°C) | Melting Point (°F) |
Duplex 2205 | 7.805 | 0.285 | 1420 – 1465 | 2588 – 2669 |
Super Duplex 2507 | 7.8 | 0.281 | 1350 | 2460 |
Standard : ASTM B564 / ASME SB564
Grades : Nickel 200 / 201, Monel 400 / K500, Inconel 600, Inconel 625, Inconel 718, Incoloy 800, Incoloy 825, Hastelloy C276 / C22, / B2, Alloy 20, Titanium Gr 2/5, Cu-Ni 90/10 (C70600), Cu-Ni 70/30 (C71500)
Dimensions : ANSI B16.11, MSS SP-79, 83, 95, 97, BS 3799
Type : Socket Weld (S/W) & SCREWED (SCRD) – NPT, BSP, BSPT / Threaded
Size : 1/2″ NB TO 4″ NB
Pressure : 2000LBS, 3000LBS, 6000LBS, 9000LBS, etc
Non-destructive testing includes:
Destructive testing includes:
Grade | C | Mn | Si | S | Cu | Fe | Ni | Cr |
Nickel 200 | 0.15 max | 0.35 max | 0.35 max | 0.01 max | 0.25 max | 0.40 max | 99.0 min | - |
Nickel 201 | 0.02 max | 0.35 max | 0.35 max | 0.01 max | 0.25 max | 0.40 max | 99.0 min | - |
Inconel 600 | 0.15 max | 1.00 max | 0.50 max | 0.015max | 0.50 max | 6.00 – 10.00 | 72.00 min | 14.00 – 17.00 |
Inconel 601 | 0.10 max | 1.0 max | 0.5 max | 0.015 max | 1.0 max | Balance | 58.0 – 63.0 | 21.0 – 25.0 |
Inconel 625 | 0.10 max | 0.50 max | 0.50 max | 0.015 max | - | 5.0 max | 58.0 min | 20.0 - 23.0 |
Inconel 718 | 0.08 max | 0.35 max | 0.35 max | 0.015 max | 0.30 max | - | 50.00 - 55.00 | 17.00 - 21.00 |
Incoloy 800 | 0.10 max | 1.50 max | 1.00 max | 0.015 max | 0.75 max | 39.50 min | 30.00 – 35.00 | 19.00 – 23.00 |
Incoloy 800H | 0.05 – 0.10 | 1.50 max | 1.00 max | 0.015 max | 0.75 max | 39.50 min | 30.00 – 35.00 | 19.00 – 23.00 |
Incoloy 800HT | 0.06 – 0.10 | 1.50 max | 1.00 max | 0.015 max | 0.75 max | 39.50 min | 30.00 – 35.00 | 19.00 – 23.00 |
Incoloy 825 | 0.05 max | 1.00 max | 0.5 max | 0.03 max | 1.50 – 3.00 | 22.00 min | 38.00 – 46.00 | 19.50 – 23.50 |
Monel 400 | 0.30 max | 2.00 max | 0.50 max | 0.024 max | 28.00 – 34.00 | 2.50 max | 63.00 min | - |
Monel K500 | 0.25 max | 1.5 max | 0.5 max | 0.010 max | 27.00 – 33.00 | 0.5 – 2 | 63.00 min | - |
Hastelloy C276 | 0.010 max | 1.00 max | 0.08 max | 0.03 max | - | 4.00 – 7.00 | 50.99 min* | 14.50 – 16.50 |
Hastelloy C22 | 0.010 max | 0.50 max | 0.08 max | 0.02 max | - | 2.00 – 6.00 | 50.015 min* | 20.00 – 22.50 |
Hastelloy B2 | 0.02 max | 1.0 max | 0.1 max | 0.03 max | - | 2.0 max | Bal | 1.0 max |
Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
Nickel 200 / 201 | 8.9 g/cm3 | 1446 °C (2635 °F) | Psi – 67000 , MPa – 462 | Psi – 21500 , MPa – 148 | 45 % |
Inconel 600 | 8.47 g/cm3 | 1413 °C (2580 °F) | Psi – 95,000 , MPa – 655 | Psi – 45,000 , MPa – 310 | 40 % |
Inconel 601 | 8.1 g/cm3 | 1411 °C (2571 °F) | Psi – 80,000 , MPa – 550 | Psi – 30,000 , MPa – 205 | 30 % |
Inconel 625 | 8.4 g/cm3 | 1350 °C (2460 °F) | Psi – 1,35,000 , MPa – 930 | Psi – 75,000 , MPa – 517 | 42.5 % |
Inconel 718 | 8.2 g/cm3 | 1350 °C (2460 °F) | Psi – 1,35,000 , MPa – 930 | Psi – 75,000 , MPa – 482 | 45 % |
Incoloy 800/H/HT | 7.94 g/cm3 | 1385 °C (2525 °F) | Psi – 75,000 , MPa – 520 | Psi – 30,000 , MPa – 205 | 30 % |
Incoloy 825 | 8.14 g/cm3 | 1400 °C (2550 °F) | Psi – 80,000 , MPa – 550 | Psi – 32,000 , MPa – 220 | 30 % |
Monel 400 | 8.8 g/cm3 | 1350 °C (2460 °F) | Psi – 80,000 , MPa – 550 | Psi – 35,000 , MPa – 240 | 40 % |
Monel K500 | 8.44 g/cm3 | 1350 °C (2460 °F) | Psi – 160000 , MPa – 1100 | Psi – 115000 , MPa – 790 | 20 % |
Hastelloy C276 | 8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40 % |
Hastelloy C22 | 8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000 , MPa – 690 | Psi – 45000 , MPa – 310 | 45 % |
Hastelloy B2 | 9.2 g/cm3 | 1370 °C (2500 ºF ) | Psi – 1,10,000 , MPa – 760 | Psi – 51000 , MPa – 350 | 40 % |
Grade : ASTM A105 Gr 70, ASTM A350 Grade LF1, LF2, LF3 / ASTM A694 Gr F42, F46, F48, F50, F52, F56, F60, F65, F70
Dimensions : ANSI B16.11, MSS SP-79, 83, 95, 97, BS 3799
Type : Socket Weld (S/W) & SCREWED (SCRD) – NPT, BSP, BSPT / Threaded
Size : 1/2″ NB TO 4″ NB
Pressure : 2000LBS, 3000LBS, 6000LBS, 9000LBS, etc
Manufactured Forged Socketweld Fittings go with quality assurance test under professionals some of the tests are:
Element | C | Mn | Si | Ph | Su | Mo | Cr | Ni |
Carbon Steel | 0.08 – 0.15 | 0.30 – 0.60 | 0.15 – 0.50 | 0.025 max * | 0.025 max * | 0.90 – 1.10 | 2.00 – 2.50 | 0.5 max |
Property | Ultimate Tensile Strength * | 0.2 % Yield Strength * | Elongation * | Reduction of Area * | Charpy Impact Toughness | Hardness (Brinell) |
Values | 95 min Ksi (655 Mpa) | 75 min Ksi (517 Mpa) | 17 % min | 35 % min | 42 mean/ 33 min J at –18o C | 197 – 237 BHN (75 Ksi min) |
Standard : ASTM A182 / ASME SA1824
Grades : A182 Grade F1, F2, F5, F9, F11, F12, F22, F91
Dimensions : ANSI B16.11, MSS SP-79, 83, 95, 97, BS 3799
Type : Socket Weld (S/W) & SCREWED (SCRD) – NPT, BSP, BSPT / Threaded
Size : 1/2″ NB TO 4″ NB
Pressure : 2000LBS, 3000LBS, 6000LBS, 9000LBS, etc
Manufactured Forged Socketweld Fittings go with quality assurance test under professionals some of the tests are:
Chemical Composition of ASTM A182 Low Alloy Steels, % | ||||||||
Grades | C | Mn | P | S | Si | Cr | Mo | Others |
F1 |
0.28 | 0.60-0.90 | 0.045 | 0.045 | 0.15-0.35 | - | 0.44-0.65 | - |
F2 | 0.05-0.21 | 0.60-0.80 | 0.040 | 0.040 | 0.10-0.60 | 0.50-0.81 | 0.44-0.65 | - |
F5 | 0.15 | 0.30-0.60 | 0.030 | 0.030 | 0.50 | 4.0-6.0 | 0.44-0.65 | *A |
F9 | 0.15 | 0.30-0.60 | 0.030 | 0.030 | 0.50-1.00 | 8.0-10.0 | 0.90-1.10 | - |
F11 | 0.05-0.15 | 0.3-0.6 | 0.03 | 0.03 | 0.5-1 | 1-1.5 | 0.044-0.65 | *C |
F12 | 0.15 max | 0.3-0.6 | 0.03 | 0.03 | 0.5 | 4-6 | 0.44-0.65 | - |
F22 | 0.05-0.15 | 0.3-0.6 | 0.045 | 0.03 | 0.5 | 0.8-1.25 | 0.44-0.65 | - |
F91 | 0.08-0.12 | 0.30-0.60 | 0.020 | 0.010 | 0.20-0.50 | 8.0-9.5 | 0.85-1.05 | *D |
F92 | 0.07-0.13 | 0.30-0.60 | 0.020 | 0.010 | 0.50 | 8.5-9.5 | 0.30-0.60 | *E |
Chemical Composition Ranges and Limits, percent | ||||||||
AISI Number | C | Mn | P Max. |
S Max. |
Si |
Ni |
Cr |
Mo |
AISI 4130 | 0.28/0.33 | 0.40/0.60 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4137 | 0.35/0.40 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4140 | 0.38/0.43 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4142 | 0.40/0.45 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4145 | 0.43/0.48 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4147 | 0.45/0.50 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4150 | 0.48/0.53 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15/0.25 |
AISI 4161 | 0.56/0.64 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | 0.25/0.35 |
AISI 4320 | 0.17/0.22 | 0.45/0.65 | 0.035 | 0.040 | 0.20/0.35 | 1.65/2.00 | 0.40/0.60 | 0.20/0.30 |
AISI 4340 | 0.38/0.43 | 0.60/0.80 | 0.035 | 0.040 | 0.20/0.35 | 1.65/2.00 | 0.70/0.90 | 0.20/0.30 |
AISI 4419 | 0.18/0.23 | 0.45/0.65 | 0.035 | 0.040 | 0.20/0.35 | --- | --- | 0.45/0.60 |
AISI 4615 | 0.13/0.18 | 0.45/0.65 | 0.035 | 0.040 | 0.20/0.35 | 1.65/2.00 | --- | 0.20/0.30 |
AISI 4620 | 0.17/0.22 | 0.45/0.65 | 0.035 | 0.040 | 0.20/0.35 | 1.65/2.00 | --- | 0.20/0.30 |
AISI 4621 | 0.18/0.23 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 1.65/2.00 | --- | 0.20/0.30 |
AISI 4626 | 0.24/0.29 | 0.45/0.65 | 0.035 | 0.040 | 0.20/0.35 | 0.70/1.00 | --- | 0.15/0.25 |
AISI 4718 | 0.16/0.21 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.90/1.20 | 0.35/0.55 | 0.30/0.40 |
AISI 4720 | 0.17/0.22 | 0.50/0.70 | 0.035 | 0.040 | 0.20/0.35 | 0.90/1.20 | 0.35/0.55 | 0.15/0.25 |
AISI 4815 | 0.13/0.18 | 0.40/0.60 | 0.035 | 0.040 | 0.20/0.35 | 3.25/3.75 | --- | 0.20/0.30 |
AISI 4817 | 0.15/0.20 | 0.40/0.60 | 0.035 | 0.040 | 0.20/0.35 | 3.25/3.75 | --- | 0.20/0.30 |
AISI 4820 | 0.18/0.23 | 0.50/0.70 | 0.035 | 0.040 | 0.20/0.35 | 3.25/3.75 | --- | 0.20/0.30 |
AISI 5120 | 0.17/0.22 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | --- |
AISI 5130 | 0.28/0.33 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | --- |
AISI 5132 | 0.30/0.35 | 0.60/0.80 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.75/1.00 | --- |
AISI 5135 | 0.33/0.38 | 0.60/0.80 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.05 | --- |
AISI 5140 | 0.38/0.43 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | --- |
AISI 5145 | 0.43/0.48 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | --- |
AISI 5147 | 0.46/0.51 | 0.70/0.95 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.85/1.15 | --- |
AISI 5150 | 0.48/0.53 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | --- |
AISI 5155 | 0.51/0.59 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.70/0.90 | --- |
AISI 6150 | 0.48/0.53 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | --- | 0.80/1.10 | 0.15 min. |
AISI 8615 | 0.13/0.18 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8617 | 0.15/0.20 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8620 | 0.18/0.23 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8622 | 0.20/0.25 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8625 | 0.23/0.28 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8627 | 0.25/0.30 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8630 | 0.28/0.33 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8637 | 0.35/0.40 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8640 | 0.38/0.43 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8642 | 0.40/0.45 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8645 | 0.43/0.48 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8655 | 0.51/0.59 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.15/0.25 |
AISI 8720 | 0.18/0.23 | 0.70/0.90 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.20/0.30 |
AISI 8740 | 0.38/0.43 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.20/0.30 |
AISI 8822 | 0.20/0.25 | 0.75/1.00 | 0.035 | 0.040 | 0.20/0.35 | 0.40/0.70 | 0.40/0.60 | 0.30/0.40 |
AISI 9254 | 0.51/0.59 | 0.60/0.80 | 0.035 | 0.040 | 1.20/1.60 | 0.60/0.80 | --- | --- |
AISI 9255 | 0.51/0.59 | 0.70/0.95 | 0.035 | 0.040 | 1.80/2.20 | --- | --- | --- |
AISI 9260 | 0.56/0.64 | 0.75/1.00 | 0.035 | 0.040 | 1.80/2.20 | --- | --- | --- |
Mechanical Properties of ASTM A182 Low Alloy Steels | |||||
Grade | Tensile Strength min. ksi[MPa] |
Yield Strength min. ksi[MPa] |
Elongation, min. % | Reduction of Area, min. % |
Brinell Hardness Number, HBW |
F1 | 70[485] | 40[275] | 20 | 30 | 143-192 |
F2 | 70[485] | 40[275] | 20 | 30 | 143-192 |
F5 | 70[485] | 40[275] | 20 | 35 | 143-217 |
F5a | 90[620] | 65[450] | 22 | 50 | 187-248 |
F9 | 85[585] | 55[380] | 20 | 40 | 179-217 |
F11 | 90[620] | 64[440] | 18 | 40 | 187-248 |
F91 | 90[620] | 60[415] | 20 | 40 | 190-248 |
F92 | 90[620] | 64[440] | 20 | 45 | ≤269 |